Origin	China
Model Number	SJ101, SJ201, SJ301, SJ501,SJ503etc

Submerged Arc Welding Fluxes: Aggolomerated Flux Series

Description	Flux Type	Matched Welding Wire	Applicable Base Metal	Main Application
SJ101	Fluorride-Basic FB	H08A, H08MnA, H10Mn2	Carbon Steel, Low Alloy Steel	Pressure Vessels, Ships, Welded pipes and steel structures etc.
SJ101G	Fluorride-Basic FB	H08MnA, H10Mn2	Pipe Steel, Low Alloy Steel	Pressure Vessels, Bridges, Welded pipes etc.
SJ102	Fluorride-Basic FB	H08MnA, H10Mn2	Carbon Steel, Low Alloy Steel	Pressure Vessels, Ships, Welded pipes and steel structures etc.
SJ201	Aluminum-Basic AB	H08MnA	Carbon Steel	Welded Pipes, Oil Pipes and steel structures etc. Used in high speed and large scale.
SJ301	Calcium-Silicon CS	H08A, H08MnA, H08MnMoA	Carbon Steel, Low Alloy Steel	Welded Pipes, Oil Pipes, pressure vessel and steel structures etc.
SJ401	Manganese-Silicate MS	H08A, H08MnA	Mild Steel and Low Alloy Steel	Steel structures, structure for vehicles and mining machinery.
SJ501	Aluminate-Rutile AR	H08A, H08MnA, H08MnMoA	Mild Steel and Low Alloy Steel	Shipbuilding, Boilers, Pressure vessels etc.
SJ503	Aluminate-Rutile AR	H08A, H08MnA	Mild Steel and Low Alloy Steel	Steel structure, pressure vessels etc.
SJ111	Fluorride-Basic FB	H1Cr13, H2Cr13	Alloy Steel	Cladding of joint-casting and supporting rollers

1. SJ101: Being defined as a Fluorine-Alkali type of bonded flux, with alkality degree of 1.80

2. SJ102: Being defined as a Fluorine-Alkali type of bonded flux, with alkality degree of 3.50 and especially high impact tenacity.

3. SJ301: Being defined as a silicon-calcium type of mild bonded flux, with alkality degree of 1.00Being suitable for common steel constrcures, boiler steel constructure and pipe line etc.

4. SJ401: Being defined as a silicon-manganese type of acid bonded flux, with alkality degree of 0.60. Widely being applied to weld low carbon and some low alloy steel.

5. SJ403: Being defined as a silicon-manganese type of acid bonded flux, with strong ability of anti-rust, being not sensitive to the rusty marks, oxidation films and oil contamination.

6. SJ501: Being defined as an alumium-titanium type of acid bonded flux, with alkality degree of 05-0.8 and strong ability of anti-airhole, and the specific gravity being small when loose loaded.

7. SJ601: Being defined as a alkality type of bonded flux, with alkality degree of 1.80. Especially being used to weld important structure of stainless steel and high alloy steel

The above are some of our main welding fluxes for Submerged Arc Welding. We can also produce the fluxes according to buyer's specific proportion.

REMARKS:
1. Before welding, fluxes need to be baked for two hours at 300-500 degree.
2. Removal of rust, oil, dirt, water, impurities etc. In welding-area is required.

Product Specification/Models
SJ101, SJ101G, SJ102, SJ201, SJ301, SJ401, SJ501, SJ503, SJ111

Application
1.Pressure Vessels, Ships, Welded pipes and steel structures etc.
2.Welded Pipes, Oil Pipes and steel structures etc. Used in high speed and large scale.
3.Steel structures, structure for vehicles and mining machinery.
4.Cladding of joint-casting and supporting rollers.

Other Information
REMARKS:
1. Before welding, fluxes need to be baked for two hours at 300-500 degree.
2. Removal of rust, oil, dirt, water, impurities etc. In welding-area is required.